|本期目录/Table of Contents|

[1]陈锐杰,顾欧昀,廖永涛,等.基于阳极Al2O3的非涂覆式金属基体整体催化剂载体的制备[J].南京工业大学学报(自然科学版),2017,39(03):26-33.[doi:10.3969/j.issn.1671-7627.2017.03.006]
 CHEN Ruijie,GU Ouyun,LIAO Yongtao,et al.Preparation of non-coated metallic monolith catalyst support by anodization[J].Journal of NANJING TECH UNIVERSITY(NATURAL SCIENCE EDITION),2017,39(03):26-33.[doi:10.3969/j.issn.1671-7627.2017.03.006]
点击复制

基于阳极Al2O3的非涂覆式金属基体整体催化剂载体的制备()
分享到:

《南京工业大学学报(自然科学版)》[ISSN:1671-7627/CN:32-1670/N]

卷:
39
期数:
2017年03期
页码:
26-33
栏目:
出版日期:
2017-05-20

文章信息/Info

Title:
Preparation of non-coated metallic monolith catalyst support by anodization
文章编号:
1671-7627(2017)03-0026-08
作者:
陈锐杰1顾欧昀1廖永涛1李华波2樱井诚3周吕1马华1郭燏1
1.南京工业大学 化工学院 材料化学工程国家重点实验室,江苏 南京 210009; 2.四川蜀泰化工科技有限公司,四川 遂宁 629300; 3.日本东京农工大学 化学工学科,日本 东京 184-8588
Author(s):
CHEN Ruijie1GU Ouyun1LIAO Yongtao1LI Huabo2SAKURAI Makoto3ZHOU Lyu1MA Hua1GUO Yu1
1.State Key Laboratory of Materials-Oriented Chemical Engineering,College of Chemical Engineering, Nanjing Tech University, Nanjing 210009,China; 2.Sichuan Shutai Chemical Technology Co.Ltd., Suining 629300,China; 3.Department of Chemical Engineering, Tokyo University of Agriculture and Technology,Tokyo 184-8588,Japan
关键词:
催化剂载体 Al2O3 阳极氧化 非涂覆整体式催化剂
Keywords:
catalyst support Al2O3 anodization non-coated monolith catalyst
分类号:
TQ426.65
DOI:
10.3969/j.issn.1671-7627.2017.03.006
文献标志码:
A
摘要:
通过草酸溶液中的二步氧化法制备多孔阳极Al2O3(PAA)膜。在保持金属一体化结构下,考察阳极氧化条件(电压、时间、电解液浓度及温度)对多孔Al2O3膜的结构特性的影响。在80 ℃下对PAA膜进行水热处理1.5 h并在500 ℃下焙烧3 h。结果表明:孔径和膜厚随电压(或电解质浓度、阳极氧化时间)增加呈线性增长,孔径(或膜厚)和电解液温度呈指数型关系,孔密度和电压关系亦然; 另一方面,氧化时间、电解液温度、电解液浓度对孔密度几乎没影响; 平板的表面积最大可提高到3 200倍,提高电解液的温度被认为是扩大表面积最有效的方法。水热处理后表面积可以从13.5 m2/g增加到180.3 m2/g,并将无定形骨架Al2O3转变为γ-Al2O3。通过阳极氧化-水热处理-焙烧制得的锯齿状蜂窝体与商业的堇青石蜂窝体相比,比表面积略高,有更大的开孔率和更轻的质量。
Abstract:
Porous anodic alumina(PAA)films were prepared by a two-step anodization in oxalic acid. The effect of anodizing conditions(voltage, time, electrolyte concentration, and temperature)on structural features was investigated under the metallic monolith structure. PAA film was treated hydrothermally for 1.5 h at 80 ℃, then roasted 3 h at 500 ℃. Results showed that pore diameter and film thickness increased linearly with the increase of anodization voltage(or electrolyte concentration, or anodization time). Exponential relations between pore diameter(or film thickness)and electrolyte temperature, and between pore density and voltage were confirmed. No effect of anodization time, temperature and concentration of the electrolyte on pore density was found. The surface area of the plate could be increased to 3 200 times, and the electrolyte temperature were considered to be the most effective factor to enlarge the surface area. When the PAA was subjected into hot water at 80 ℃ for 1.5 h, its surface area increased from 13.5 m2/g to 180.3 m2/g, accompany with the transformation of alumina from amorphous to gamma form. The serrated honeycomb prepared with "anodization-hydrothermal treatment-calcination" had higher surface area, bigger open frontal area and smaller bulk density than commercial cordierite honeycomb.

参考文献/References:

[1] 黄琼,马文娇,张志远,等.堇青石负载Mn-Zn-O复合金属氧化物的甲苯催化燃烧性能[J].南京工业大学学报(自然科学版),2011,33(4):7.
[2] SAMAD J E,NYCHKA J A,SEMAGINA N V.Structured catalysts via multiple stage thermal oxidation synthesis of FeCrAl alloy sintered microfibers[J].Chemical engineering journal,2011,168:470.
[3] MA Y,CHEN M,SONG C,et al.Catalytic oxidation of toluene,acetone and ethyl acetate on a new Pt-Pd/stainless steel wire mesh catalyst[J].Acta physico-chimica sinica,2008,24(7):1132.
[4] RUI Z,CHEN C,LU Y,et al.Anodic alumina supported Pt catalyst for total oxidation of trace toluene[J].Chinese journal of chemical engineering,2014,22:882.
[5] SÁNCHEZ M J F,BOLDRINI D E,TONETTO G M,et al.Palladium catalyst on anodized aluminum monoliths for the partial hydrogenation of vegetable oil[J].Chemical engineering journal,2011,167:355.
[6] LYU Z,ZHANG F Z,LEI X D,et al.In situ growth of layered double hydroxide films on anodic aluminum oxide/aluminum and its catalytic feature in aldol condensation of acetone[J].Chemical engineering science,2008,63:4055.
[7] FANG Y,LV Y,CHE R C,et al.Two-dimensional mesoporous carbon nanosheets and their derived graphene nanosheets:synthesis and efficient lithium ion storage[J].Journal of the American chemical society,2013,135:1524.
[8] ZARASKA L,STEPNIOWSKI W J,JASKULAA M,et al.Analysis of nanopore arrangement of porous alumina layers formed by anodizing in oxalic acid at relatively high temperatures[J].Applied surface science,2014,305:650.
[9] ANNA B,AGNIESZKA B,GRZEGORZ D S.Effect of processing parameters on pore opening and mechanism of voltage pulse detachment of nanoporous anodic alumina[J].Electrochimica acta,2015,178:374.
[10] XU Y,THOMPSON G E,WOOD G C.Mechanism of anodic film growth on aluminium[J].Transactions of the institute of metal finishing,1985,63:98.
[11] 李良方.电压和电解液对阳极氧化铝模板孔间距的影响[D].内蒙古:内蒙古科技大学,2013.
[12] ECHAVE F J,SANZ O,VELASCO I,et al.Effect of the alloy on micro-structured reactors for methanol steam reforming[J].Catalysis today,2013,213:145.
[13] KOLODZIEIJ A,LOJEWSKA J.Short-channel structured reactor for catalytic combustion:design and evaluation[J].Chemical engineering and processing,2007,46(7):637.

备注/Memo

备注/Memo:
收稿日期:2016-01-10
基金项目:国家自然科学基金(21403108); 江苏高校优势学科建设工程
作者简介:陈锐杰(1990—),男,江苏南京人,硕士,主要研究方向为环保催化材料; 郭燏(联系人),教授,E-mail: mguoyu@njtech.edu.cn.
引用本文:陈锐杰,顾欧昀,廖永涛,等.基于阳极Al2O3的非涂覆式金属基体整体催化剂载体的制备[J].南京工业大学学报(自然科学版),2017,39(3):26-33..
更新日期/Last Update: 2017-05-31