Title:
Synthesis of multifunctional UV-curable rosin alcohol-based polyurethane acrylate
文章编号:
1671-7627(2017)02-0011-05
作者:
王同庆谢晖黄莉吴笑天
南京工业大学 化工学院,江苏 南京 210009
Author(s):
WANG TongqingXIE HuiHUANG LiWU Xiaotian
College of Chemical Engineering,Nanjing Tech University,Nanjing 210009,China
关键词:
UV固化 松香醇 聚氨酯丙烯酸酯
Keywords:
UV-curing rosin alcohol polyurethane acrylate
分类号:
O636
DOI:
10.3969/j.issn.1671-7627.2017.02.003
文献标志码:
A
摘要:
以饱和松香三元醇为原料合成的松香醇基端羟基聚酯(RAPE)、异氟尔酮二异氰酸酯(IPDI)和季戊四醇三丙烯酸酯(PETA)为原料,通过本体聚合法,两步反应合成新型九官能的松香醇基聚氨酯丙烯酸酯(RAPUA),采用傅里叶红外光谱仪(FT-IR)对其结构进行表征,结果表明得到目标产物。研究反应温度、催化剂用量、阻聚剂用量等对合成RAPUA的影响,考察固化涂膜的铅笔硬度、附着力、耐冲击性、耐候性等性能。通过实验确定了最佳的合成工艺条件:第1步反应温度55 ℃、催化剂用量0.6%、反应时间2.5 h; 第2步反应温度75 ℃、催化剂用量0.8%、反应时间3 h、阻聚剂用量为体系总质量的0.3%。在此工艺条件下,涂膜的铅笔硬度达6H、附着力达1级、耐冲击性达48 cm、耐候性优良。
Abstract:
The new nine-functional rosin alcohol-based polyurethane acrylate(RAPUA)was synthesized from two-step reaction by bulk polymerization with rosin alcohol-based polyester synthesized from the saturated rosin trihydric alcohol,isophorone diisocyanate(IPDI),and pentaerythritol three acrylate(PETA).The obtained target product was characterized by Fourier transform infrared spectrometer(FT-IR)for its structure.The effects of reaction temperature,catalyst amount and polymerization inhibitor amount on the synthesis of RAPUA were discussed.The coating properties of RAPUA,such as pencil hardness,adhesive force,impact resistance,and weatherability were investigated.The optimal synthetic conditions for the title compound were the first step reaction temperature of 55 ℃,catalyst amount of 0.6%,and reaction time of 2.5 h and the second step reaction temperature of 75 ℃,catalyst amount of 0.8%,reaction time of 3 h,and polymerization inhibitor amount of 0.3%.Under the optimal conditions,the pencil hardness of RAPUA film was 6H,adhesion grade was 1,and impact index was 48 cm.The RAPUA film had a good weatherability.

参考文献/References:

[1] 杨政险,张爱清.光固化聚氨酯丙烯酸酯预聚物合成工艺的探讨[J].聚氨酯工业,2004,19(4):41.
[2] 郑友明,胡孝勇.新型紫外光固化聚氨酯丙烯酸酯涂料的研究进展[J].涂料工业,2012,42(10):73.
[3] WANG F,HU J Q,TU W P.Study on microstructure of UV-curable polyurethane acrylate films[J].Progress in organic coatings,2008,62(3):245.
[4] YANG Z L,WICKS D A,YUAN J J.Newly UV-curable polyurethane coatings prepared by multifunctional thiol-and ene-terminated polyurethane aqueous dispersions:photopolymerization properties[J].Polymer,2010,51:1572.
[5] 施海松,黄莉,谢晖,等.紫外光固化松香基聚氨酯丙烯酸酯的合成[J].涂料工业,2010,40(12):37.
[6] 曾韬,尹斌,陈朱辉.一种松香醇的制备方法:103952082A[P].2014-07-30.
[7] 黄坤,夏建陵.一种饱和松香三元醇及其制备方法和应用:102531840[P].2012-07-04.
[8] 李绍雄,刘益军.聚氨酯树脂及其应用[M].北京:化学工业出版社,2002:710-712.
[9] 商武,袁腾,王邦清,等.UV固化聚酯型聚氨酯丙烯酸酯低聚物的制备研究[J].热固性树脂,2013,28(6):14.
[10] 王邦清.聚酯型聚氨酯丙烯酸酯的合成及应用[D].广州:华南理工大学,2012.

相似文献/References:

[1]康小孟,黄 莉,谢 晖,等.紫外光固化松节油聚氨酯丙烯酸酯的合成[J].南京工业大学学报(自然科学版),2009,31(02):25.
 KANG Xiao meng,HUANG Li,XIE Hui,et al.Synthesis of UVcurable turpentine polyurethane acrylate[J].Journal of NANJING TECH UNIVERSITY(NATURAL SCIENCE EDITION),2009,31(02):25.
[2]刘盼盼,谢晖,黄莉,等.DCPD改性UV固化水性聚氨酯丙烯酸酯的合成[J].南京工业大学学报(自然科学版),2018,40(03):24.[doi:10.3969/j.issn.1671-7627.2018.03.005]
 LIU Panpan,XIE Hui,HUANG Li,et al.The synthesis of DCPD modified UV curable waterborne polyurethane acrylate[J].Journal of NANJING TECH UNIVERSITY(NATURAL SCIENCE EDITION),2018,40(02):24.[doi:10.3969/j.issn.1671-7627.2018.03.005]

备注/Memo

备注/Memo:
收稿日期:2015-09-30
作者简介:王同庆(1989—),男,山东鄄城人,硕士,主要研究方向为生物资源的综合开发与利用; 谢晖(联系人),教授,E-mail:xiehui@njtech.edu.cn.
引用本文:王同庆,谢晖,黄莉,等.多官能UV固化松香醇基聚氨酯丙烯酸酯的合成[J].南京工业大学学报(自然科学版),2017,39(2):11-15..
更新日期/Last Update: 2017-03-20