[1]刘杏杏,陆伟东,姜海峰,等.考虑应力影响的杉木力学性能微钻阻力检测[J].南京工业大学学报(自然科学版),2018,40(04):65-70.[doi:10.3969/j.issn.1671-7627.2018.04.011]
 LIU Xingxing,LU Weidong,JIANG Haifeng,et al.Micro-drilling resistance testing of fir mechanical properties under stress[J].Journal of NANJING TECH UNIVERSITY(NATURAL SCIENCE EDITION),2018,40(04):65-70.[doi:10.3969/j.issn.1671-7627.2018.04.011]
点击复制

考虑应力影响的杉木力学性能微钻阻力检测()
分享到:

《南京工业大学学报(自然科学版)》[ISSN:1671-7627/CN:32-1670/N]

卷:
40
期数:
2018年04期
页码:
65-70
栏目:
出版日期:
2018-07-20

文章信息/Info

Title:
Micro-drilling resistance testing of fir mechanical properties under stress
文章编号:
1671-7627(2018)04-0065-06
作者:
刘杏杏12陆伟东1姜海峰12叶国成1
1.南京工业大学 土木工程学院,江苏 南京 211800; 2.南京工大建设工程技术有限公司,江苏 南京 211800
Author(s):
LIU Xingxing12LU Weidong1JIANG Haifeng12YE Guocheng1
1.College of Civil Engineering,Nanjing Tech University,Nanjing 211800,China; 2.Nanjing Gongda Construction Technology Co. Ltd.,Nanjing 211800,China
关键词:
杉木 微钻阻力法 力学性能 阻力值修正
Keywords:
fir micro-drilling resistance methed mechanical properties correction of resistance value
分类号:
S781
DOI:
10.3969/j.issn.1671-7627.2018.04.011
文献标志码:
A
摘要:
在役木结构构件常处于受弯、受压等受力状态,常用微钻阻力法检测木材的试验研究,该法通常没有考虑实际受力状态对阻力值的影响。本文以直径15 cm、高度40 cm杉木试件作为研究对象,首先,通过对无应力状态下杉木试件的微钻阻力试验研究,获得微钻阻力值与木材密度、顺纹抗压强度、顺纹抗压弹性模量及抗弯强度之间的回归方程; 然后,对处于压应力状态下的杉木试件进行微钻阻力试验,得到随着应力等级的提升,微钻阻力值呈上升趋势; 最后,提出了考虑应力影响的杉木微钻阻力值修正系数及修正后的回归方程。
Abstract:
The in-service timber members were often under bending,compression and other stress states.Experimental studies on wood testing with the existing micro-drill resistance method were generally carried out without considering the impact of the actual stress state on the resistance value. In the paper,15 cm in diameter and 40 cm in height fir was chosen as the specimen.The regression equation between the micro-drill resistance value and wood density,compression strength parallel to grain,flexural strength and compressive elastic modulus of wood were obtained through the micro-drill resistance test under non-stress state.The micro-drill resistance test was conducted on the fir under compressive stress.Results showed that with the increasing of stress level,the micro-drill resistance value showed a rising trend.The correction coefficient of micro-drilling resistance value and the modified regression equation of fir with considering the influence of stress were proposed.

参考文献/References:

[1] 张训亚,殷亚芳.两种无损检测法评估人工林杉木抗弯性质[J].建筑材料学报,2010,13(6):836.
[2] KAHL T,WIRTH C,MUND M,et al.Using drill resistance to quantify the density in coarse woody debris of Norway spruce[J].European journal of forest research,2009,128(5):467.
[3] 孙燕良.基于微钻阻力的古建筑木材密度与力学性能检测研究[D].北京:北京林业大学,2012.
[4] 黄荣凤,王晓欢,李华,等.古建筑木材内部腐朽状况阻力仪检测结果的定量分析[J].北京林业大学学报,2008,29(6):167.
[5] 张晋,王亚超,许清风,等.基于无损检测的超役黄杉和杉木构件的剩余强度分析[J].中南大学学报(自然科学版),2011,42(12):3864.
[6] LIN C J,WANG S Y,LIN F C,et al.Effect of moisture content on the drill resistance value in Taiwania plantation wood[J].Wood and fiber science,2003,35(2):234.
[7] 中华人民共和国国家质量监督检验检疫总局.木材物理力学试验方法总则:GB/T 1928—2009[S].北京:中国标准出版社,2009.
[8] 中华人民共和国国家质量监督检验检疫总局.木材密度测定方法:GB/T 1933—2009[S].北京:中国标准出版社,2009.
[9] 中华人民共和国国家质量监督检验检疫总局.木材含水率测定方法:GB/T1931—2009[S].北京:中国标准出版社,2009.
[10] 中华人民共和国国家质量监督检验检疫总局.木材顺纹抗压强度试验方法:GB/T 1935—2009[S].北京:中国标准出版社,2009.
[11] 中华人民共和国国家质量监督检验检疫总局.木材顺纹抗压弹性模量测定方法:GB/T 15777—2017[S].北京:中国标准出版社,2017.
[12] 中华人民共和国国家质量监督检验检疫总局.木材抗弯强度试验方法:GB/T 1936.1—2009[S].北京:中国标准出版社,2009.

备注/Memo

备注/Memo:
收稿日期:2017-04-19
基金项目:国家自然科学基金(51678298)
作者简介:刘杏杏(1988—),男,江苏南通人,硕士,主要研究方向为木结构检测与评价; 陆伟东(联系人),教授,E-mail:wdlu@njtech.edu.cn.
引用本文:刘杏杏,陆伟东,姜海峰,等.考虑应力影响的杉木力学性能微钻阻力检测[J].南京工业大学学报(自然科学版),2018,40(4):65-70..
更新日期/Last Update: 2018-07-30