Title:
Preparation of aluminum tripolyphosphate from phosphate-potassium ore
文章编号:
1671-7627(2015)04-0104-05
作者:
王为国1李青鹏2吕仁亮2马家玉2汪铁林1王存文1
1.武汉工程大学 绿色化工过程教育部重点实验室,湖北 武汉 430073; 2.武汉工程大学 化工与制药学院,湖北 武汉 430073
Author(s):
WANG Weiguo1LI Qingpeng2LYU Renliang2MA Jiayu2WANG Tielin1WANG Cunwen1
1.Key Laboratory for Green Chemical Process of Ministry of Education,Wuhan Institute of Technology,Wuhan 430073,China; 2.School of Chemical Engineering & Pharmacy,Wuhan Institute of Technology,Wuhan 430073,China;
关键词:
磷钾伴生矿 综合利用 三聚磷酸铝
Keywords:
phosphate-potassium ore comprehensive utilization aluminum tripolyphosphate
分类号:
TQ126.3+5
DOI:
10.3969/j.issn.1671-7627.2015.04.018
文献标志码:
A
摘要:
以湖北宜昌地区磷钾伴生矿酸浸液为原料,经净化及碱液处理等工序制备Al(OH)3干胶,然后与H3PO4经中和、缩合和水化合成三聚磷酸铝,最后对合成条件进行优化。合成三聚磷酸铝优化工艺条件:Al(OH)3与60%的H3PO4按P2O5与Al2O3的摩尔比(磷铝比)3:1,中和温度70 ℃,中和时间60 min,缩合温度290 ℃,缩合时间4 h。对优化条件下得到的产品进行化学成分分析,同时采用傅里叶变换红外光谱仪(FT-IR)和X线衍射仪(XRD)对产品进行结构表征。结果表明:所得产品是三聚磷酸铝,产品主组分含量符合Q/HGY 07—1999的要求。
Abstract:
Using acid leaching liquid of phosphate-potassium ore from Yichang,Hubei Province,as raw material,dry aluminum gel was obtained through processes of purification and alkali extraction.Then the dry aluminum gel and phosphoric acid were used to synthesize aluminum tripolyphosphate by neutralization,condensation and hydration reaction.The optimum conditions for aluminum tripolyphosphate preparation were n(H3PO4):n(Al(OH)3)=3:1,temperature neutralization reaction of 70 ℃,neutralization reaction time of 60 min,condensation temperature of 290 ℃,and condensation time of 4 h.The product obtained under the optimum conditions was analyzed and its structure and morphology were characterized by X-ray diffraction(XRD)and Fourier transform infrared spectroscopy(FT-IR).Results showed that the obtained product was aluminum tripolyphosphate and met the requirements of Q/HGY 07—1999.

参考文献/References:

[1] 刘艺玮,覃远航,王存文,等.宜昌中间坪磷钾矿矿物学研究[J].矿产综合利用,2014(1):69-71.
[2] 胡波,韩效钊,肖正辉,等.我国钾长石矿产资源分布、开发利用、问题与对策[J].化工矿产地质,2005,27(1):25-32.
[3] 段欢,王存文,覃远航,等.宜昌磷钾矿反应特性和发泡特性研究[J].化工矿物与加工,2013(9):9-11.
[4] 孙雪飞,王为国,王存文.低品位磷钾矿与磷酸共浸提取磷和钾工艺研究[J].化工矿物与加工,2011(1):6-10.
[5] 周艳,张皓东,董占能.新型无毒防锈颜料三聚磷酸二氢铝研究进展[J].磷肥与复肥,2005,20(1):19-20.
[6] 黄若愚.硫酸亚铁溶液中除硅的研究[J].广州化工,2012,40(10):92-94.
[7] 孙建勋,林润雄,苗丽红,等.利用磷肥副产氟硅酸制白炭黑的氨化工艺研究[J].无机盐工业,2009,41(7):48-50.
[8] 任万平,李晓秀,张汪寿.沉积物中磷形态及影响其释放的环境因素研究进展[J].环境污染与防治,2012,34(9):53-60.
[9] 员建,苑宏英,陈轶,等.化学沉淀法回收污泥中氮磷的影响因素研究[J].环境科学与技术,2011,34(6):148-151.
[10] 殷宪国,何佩蓉,黎慧玲.复盐沉淀法脱除湿法磷酸中镁铝氟杂质的研究[J].磷肥与复肥,1998(1):23-25.
[11] 林培喜,朱玲.无机化学与分析化学[M].哈尔滨:哈尔滨工程大学出版社,2010:382.
[12] 李闪闪.防锈颜料三聚磷酸铝制备新工艺开发[D].郑州:郑州大学,2013.
[13] 袁爱群.三聚磷酸二氢铝二水物的合成工艺[J].四川化工与腐蚀控制,2000,3(3):9-12.
[14] Tricot G,Coillot D,Creton E,et al.New insights into the thermal evolution of aluminophosphate solutions:a complementary XRD and solid state NMR study[J].Journal of the European Ceramic Society,2008,28(6):1135-1141.
[15] 卢清华.运用铝土矿选矿尾矿制备功能性颜填料及其应用性能[D].长沙:中南大学,2011.

备注/Memo

备注/Memo:
收稿日期:2014-11-19
基金项目:国家自然科学基金(51274153); 湖北省自然科学基金重点项目(2011CDA120); 湖北省中低品位磷矿资源开发利用协同创新中心开放基金(P201105)
作者简介:王为国(1963—),男,江苏建湖人,副教授,硕士,主要研究方向为矿产资源的综合利用; 吕仁亮(联系人),博士,E-mail:lvrenliang@wit.edu.cn; 王存文(联系人),教授,E-mail:wangcw0120@163.com.
引用本文:王为国,李青鹏,吕仁亮,等.磷钾伴生矿制备三聚磷酸铝[J].南京工业大学学报:自然科学版,2015,37(4):104-108..
更新日期/Last Update: 2015-07-08