|本期目录/Table of Contents|

[1]郑娇玲,李伟峰,沈晓冬.梳型聚合物水泥助磨剂的合成及应用[J].南京工业大学学报(自然科学版),2015,37(01):32-37.[doi:10.3969/j.issn.1671-7627.2015.01.006]
 ZHENG Jiaoling,LI Weifeng,SHEN Xiaodong.Synthesis and application of comb polymer cement grinding aid[J].Journal of NANJING TECH UNIVERSITY(NATURAL SCIENCE EDITION),2015,37(01):32-37.[doi:10.3969/j.issn.1671-7627.2015.01.006]
点击复制

梳型聚合物水泥助磨剂的合成及应用()
分享到:

《南京工业大学学报(自然科学版)》[ISSN:1671-7627/CN:32-1670/N]

卷:
37
期数:
2015年01期
页码:
32-37
栏目:
出版日期:
2015-01-19

文章信息/Info

Title:
Synthesis and application of comb polymer cement grinding aid
文章编号:
1671-7627(2015)01-0032-06
作者:
郑娇玲李伟峰沈晓冬
南京工业大学 材料科学与工程学院 材料化学工程国家重点实验室,江苏 南京 210009
Author(s):
ZHENG JiaolingLI WeifengSHEN Xiaodong
State Key Laboratory of Materials-Oriented Chemical Engineering,College of Materials Science and Engineering,Nanjing Tech University,Nanjing 210009,China
关键词:
水泥助磨剂 梳型聚合物 助磨效果 砂浆强度
Keywords:
cement grinding aid comb polymers grinding effect mortar strength
分类号:
TQ172.463
DOI:
10.3969/j.issn.1671-7627.2015.01.006
文献标志码:
A
摘要:
采用甲氧基聚乙二醇甲基丙烯酸酯和马来酰胺酸为原料合成一种梳型聚合物水泥助磨剂,应用在水泥粉磨试验中,通过水泥细度、比表面积、粒度分布、流动性、抗压强度来综合评价其助磨性能。结果表明:助磨剂PGA2掺量为0.04%时,水泥细度降低26%左右,3~32 μm粒径颗粒含量增加,基本流动能量提高25%,透气性增加30%,压缩性降低7%以上,3 d和28 d水泥砂浆抗压强度分别提高16.72%和7.20%。
Abstract:
Comb polymer cement grinding aid was synthesized by methoxy polyethylene glycol methacrylate and maleamidic acid and used in clinker grinding text.By the cement fineness,specific surface area,particle size distribution,cement particle liquidity, and the strength of cement mortar,the performance of the grinding aid was evaluated.Results showed that when the amount of grinding aids was 0.04%,the cement fineness was improved by about 26%,increased 3~32 μm diameter particle content,the fluidity increased by 25%,the permeability increased by 30%,more than 7% lower compressibility,the compressive strength of mortar in 3 d and 28 d increased by 16.72% and 7.20%,respectively.

参考文献/References:

[1] Heller D I T,Müller T,Honert D.Cement additives based on PCE[J].ZKG International,2011(2):40-48.
[[2] Lu B I.Synergistic grinding aic and making method,involves multiplying and cement grinding aicds are not widely used in cement enterprise:CN,1990411-A[P].2007-07-14.
[[3] 卫晓慧,王自为,任建国.新型聚羧酸水泥助磨剂的合成及应用[J].混凝土,2013(2):147-151.
[[4] 张昀,徐正华,黄世伟.聚羧酸盐系水泥助磨剂的合成[J].南京工业大学学报:自然科学版,2009,31(6):73-76.
[[5] 王振华,王栋民,王启宝.ZK-RJD 高效液体高分子合成水泥助磨剂的特性及其应用[J].水泥,2010(5):10-14.
[[6] 赵计辉,王栋民,王振华.改性三乙醇胺助磨剂的性能研究及工业化大磨试验[J].水泥,2010(11):13-17.
[[7] 周明松,周莉莉,伍思龙.氧化碱木质素制备高效水泥助磨剂[J].水泥助磨剂,2013(1):32-37.
[[8] 方云辉,郑飞龙,龚明子.聚羧酸系水泥助磨剂的研究及其应用效果[J].水泥,2010(12):12-14.
[[9] 王彬,郑强,王升平.改性三乙醇胺化合物的合成及其对水泥助磨性能的影响[J].硅酸盐通报,2009,28(6):1235-1240.
[[10] 岳光亮,王晓轩,张颖.不同结构三乙醇胺系化合物的合成及其对水泥的助磨效果[J].中国粉体技术,2012,17(6):63-66.
[[11] 谢磊.酯化三乙醇胺类新型水泥助磨剂的应用研究[D].北京:北京交通大学,2010.
[[12] 张士忠,马传杰,王升平.助磨剂原材料三乙醇胺改性的试验研究[J].水泥助磨剂,2013(3):40-43.
[[13] 蔡安兰,江朝华,严生,等.助磨剂对普通硅酸盐水泥性能的影响及作用机理[J].南京化工大学学报:自然科学版,2001,23(1):50-53.
[[14] 蔡安兰.关于水泥助磨剂助磨效果表征的探讨[J].硅酸盐通报,2000,19(6):22-26.
[[15] 张少明,翟旭东,刘亚云.粉体工程[M].北京:中国建材工业出版社,1994.

备注/Memo

备注/Memo:
收稿日期:2014-06-05
基金项目:国家重点基础研究发展计划(973计划)(2009CB623100); 江苏高校优势学科建设工程; 长江学者和创新团队发展计划(IRT1146); 江苏省普通高校研究生科研创新计划(CXZZ11_0326)
作者简介:郑娇玲(1977—),女,吉林白城人,博士生,主要研究方向为新型化学建材; 沈晓冬(联系人),教授,E-mail:xdshen@njtech.edu.cn.
引用本文:郑娇玲,李伟峰,沈晓冬.梳型聚合物水泥助磨剂的合成及应用[J].南京工业大学学报:自然科学版,2015,37(1):32-37..
更新日期/Last Update: 2015-01-20