[1]王艳飞,耿鲁阳,巩建鸣.热处理对超厚板焊接残余应力影响的数值分析[J].南京工业大学学报(自然科学版),2013,35(01):1-66.[doi:10.3969/j.issn.1671-7627.2013.01.014]
 WANG Yanfei,GENG Luyang,GONG Jianming.Numerical analysis of effects of heat treatment on residual stress in butt-welded super thick plates[J].Journal of NANJING TECH UNIVERSITY(NATURAL SCIENCE EDITION),2013,35(01):1-66.[doi:10.3969/j.issn.1671-7627.2013.01.014]
点击复制

热处理对超厚板焊接残余应力影响的数值分析()
分享到:

《南京工业大学学报(自然科学版)》[ISSN:1671-7627/CN:32-1670/N]

卷:
35
期数:
2013年01期
页码:
1-66
栏目:
出版日期:
2013-01-20

文章信息/Info

Title:
Numerical analysis of effects of heat treatment on residual stress in butt-welded super thick plates
文章编号:
1671-7627(2013)01-0066-05
作者:
王艳飞耿鲁阳巩建鸣
南京工业大学 机械与动力工程学院,江苏 南京 211800
Author(s):
WANG YanfeiGENG LuyangGONG Jianming
College of Mechanical and Power Engineering, Nanjing University of Technology, Nanjing 211800, China
关键词:
超厚板 管板 焊接残余应力 变形 热处理
Keywords:
super thick plate tube sheet weld residual stress deformation heat treatment
分类号:
TG404
DOI:
10.3969/j.issn.1671-7627.2013.01.014
文献标志码:
A
摘要:
基于ABAQUS软件的热弹塑性有限元程序,对390 mm超厚度20MnMoNb钢板拼焊制造EO反应器管板的焊接过程进行焊接残余应力与变形有限元模拟,考察焊后500 ℃热处理对板内残余应力与变形的影响。结果表明:超厚板焊态在焊缝及热影响区存在高度不均匀的残余应力,由于为了限制管板的变形,在板面上施压有配重,导致先焊面的残余应力较大,特别是在靠近表面的焊缝及热影响区附近存在残余拉应力峰值; 后焊面的残余应力相对较小一些; 焊缝内部为残余压应力; 焊后管板发生了一端翘起的角变形; 500 ℃热处理可明显降低厚板的焊接残余应力,且使应力分布趋于均匀,但热处理后焊接变形有所增大。
Abstract:
Residual stress and deformation in butt-welded 390 mm 20MnMoNb super-thick plates for manufacturing the tube sheet of an EO(ethylene oxide)reactor were simulated by thermal elastic-plastic finite element program of ABAQUS software. The effects of post-welding heat treatment(PWHT)on the residual stress and deformation were analyzed. The results showed that highly non-uniform residual stress was generated in the weld metal and heat affected zone(HAZ), and the stress in the firstly welded side was higher than that in the side welded afterward due to the application of a load to restrain the welding deformation. Tensile stress peaks located at the weld metal and HAZ near the surface of the firstly welded side. Compress stress was generated in the weld root. Angular deformation occurred in the welded plates. After 500 ℃ PWHT, the residual stress was dramatically decreased and its distribution became more uniform, but the angular deformation was increased.

参考文献/References:

[1] Dong P,Zhang J.Residual stresses in strength-mismatched welds and implications on fracture behavior[J].Engineering Fracture Mechanics,1999,64(4):485-505.
[2] Hong T K,Lee Y L,Sun X J.Effects of residual stress and heat treatment on fatigue strength of weldments[J].Materials Science and Engineering:A,2008,497(1/2):37-43.
[3] 吴运祥.低合金高强钢焊接构件在高温锅炉水中的应力腐蚀开裂行为研究[J].压力容器,2010,27(6):1-6.
[4] Paddea S,Francis J A,Paradowska A M,et al.Residual stress distributions in a P91 steel-pipe girth weld before and after post weld heat treatment[J].Materials Science and Engineering:A,2012,534:663-672.
[5] Mirzaee-Sisan A,Fookes A J,Truman C E,et al.Residual stress measurement in a repair welded header in the as-welded condition and after advanced post weld treatment[J].International Journal of Pressure Vessels and Piping,2007,84(5):265-273.
[6] 徐连勇,荆洪阳,周春亮,等.焊后热处理对P92钢管道焊接残余应力场的影响[J].焊接学报,2010,31(3):13-16.
[7] Deng D,Murakawa H.Numerical simulation of temperature field and residual stress in multi-pass welds in stainless steel pipe and comparison with experimental measurements[J].Computational Materials Science,2006,37(3):269-277.
[8] 陈楚.数值分析在焊接中的应用[M].上海:上海交通大学出版社,1985.
[9] 陈祝年.焊接工程师手册[M].北京:化学工业出版社,2000.
[10] 潘家祯.压力容器材料实用手册:碳钢及合金钢[M].北京:化学工业出版社,2000.
[11] Teng T,Lin C.Effect of welding conditions on residual stress due to butt welds[J].International Journal of Pressure Vessels and Piping,1998,75(12):857-864.
[12] 蒋文春,王炳英,巩建鸣.焊接残余应力在热处理过程中的演变[J].焊接学报,2011,32(4):45-48.

备注/Memo

备注/Memo:
收稿日期:2012-03-28
基金项目:国家高技术研究发展计划(863计划)(2009AA044803)
作者简介:王艳飞(1986—),男,江苏宿迁人,博士生,主要研究方向为过程设备先进再制造和计算机辅助工程; 巩建鸣(联系人),教授,E-mail:gongjm@njut.edu.cn..
更新日期/Last Update: 2013-01-20